Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives Leisure and Sports

Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives Leisure and Sports

Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives Leisure and Sports
Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives Leisure and Sports

Product Details:

Place of Origin: Korea
Brand Name: LG CHEM
Certification: MSDS, ROHS, UL, REACH
Model Number: KEYFLEX BT 1072D

Payment & Shipping Terms:

Minimum Order Quantity: 18T
Price: NEGOTIABLE ACCORDING TO ORDER QUANTITY
Packaging Details: 25KG/BAG, 40BAGS PER PALLET
Delivery Time: 30 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT
Payment Terms: T/T
Supply Ability: 500T PER MONTH
Contact Now
Detailed Product Description
Features: High Modulus Material: TPE
Grade: Injection Molding Grade Sharp: Particles
Application: Automotives, Leisure And Sports Color: Customization
High Light:

tpe granules

,

thermoplastic elastomers tpe

Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives, Leisure and Sports.
 
KEYFLEX BT 1072D Quick Detail:  
1. Injection Molding Grade
2. General Purpose
3. High Modulus
4. Ester Type TPE

 
KEYFLEX BT 1072D Description:
Ester Type TPE KEYFLEX BT 1072D is designed for injection molding products. It exhibits an excellent characteristic of High Modulus.
 
KEYFLEX BT 1072D Applications:
Automotives,Leisure & Sports.
 
KEYFLEX BT 1072D Datasheet:

PropertiesTest ConditionTest MethodUnitTypical Value
Physical    
Specific Gravity ASTM D792-1.26
Molding Shrinkage (Flow), 3.2mm ASTM D955%1.5 ~ 1.9
Melt Flow Rate240℃/2.16kgASTM D1238g/10min26
Water Absorption23℃, 24hrsASTM D570%0.3
Mechanical    
Tensile Strength, 2mm ASTM D638  
@ Yield50mm/min kg/cm2300
@ Break50mm/min kg/cm2500
Tensile Elongation, 2mm ASTM D638  
@ Yield50mm/min % 
@ Break50mm/min %600
Flexural Strength, 6.4mm15mm/minASTM D790kg/cm2 
Flexural Modulus, 6.4mm15mm/minASTM D790kg/cm26,800
Tear Strength @ Break50mm/minASTM D624kg/cm165
IZOD Impact Strength, 6.4mm ASTM D256  
(Notched)23℃ kg·cm/cm10
 -40℃ kg·cm/cm3.5
Shore HardnessShore DASTM D2240-67
Shore HardnessShore AASTM D2240- 
Thermal    
Melt Temperature @ Peak ASTM D3418220
Heat Deflection Temperature, 6.4mm ASTM D648  
(Unannealed)4.6kg 125
Flammability UL94  
1.5mm  classHB
3.0mm  classHB
Electrical    
Comparative Tracking Index(CTI)Solution AIEC 60112Volts600
Surface Resistivity IEC 60093Ohm 
Volume Resistivity23℃ASTM D257Ohm·m>E11
Dielectric Strength, 1mm23℃ASTM D149kV/mm26
Dielectric Constant (106 Hz)23℃ASTM D150sec 

 
KEYFLEX BT 1072D Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2.KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM
6. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
FOR MORE INFORMATION, PLEASE CONTACT US.

Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives Leisure and Sports 0Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives Leisure and Sports 1Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives Leisure and Sports 2Ester Type TPE KEYFLEX BT 1072D TPE Raw Material with High Modulus for Automotives Leisure and Sports 3

Contact Details
EVER BEST(HK) LIMITED

Contact Person: Zhu

Tel: +8615862380120

Send your inquiry directly to us (0 / 3000)

Other Products
Request A Quote

E-Mail | Sitemap

Privacy Policy China Good Quality ABS Plastic Raw Material Supplier. © 2020 - 2021 polymer-plastic.com. All Rights Reserved.