Good Toughness Polycarbonate Raw Material For IT/OA LUPOY SP2053

Good Toughness Polycarbonate Raw Material For IT/OA LUPOY SP2053

    • Good Toughness Polycarbonate Raw Material For IT/OA LUPOY SP2053
    • Good Toughness Polycarbonate Raw Material For IT/OA LUPOY SP2053
    • Good Toughness Polycarbonate Raw Material For IT/OA LUPOY SP2053
  • Good Toughness Polycarbonate Raw Material For IT/OA LUPOY SP2053

    Product Details:

    Place of Origin: Korea
    Brand Name: LG CHEM
    Certification: MSDS, ROSH,UL
    Model Number: SP2053

    Payment & Shipping Terms:

    Minimum Order Quantity: 16T
    Price: NEGOTIABLE ACCORDING TO ORDER QUANTITY
    Packaging Details: 25KG/BAG, 40BAGS PER PALLET
    Delivery Time: 20 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT
    Payment Terms: T/T
    Supply Ability: 500T PER MONTH
    Contact Now
    Detailed Product Description
    Place Of Origin: Guangdong,China(Mainland) Brand Nmae: LG CHEM
    Material: Polycarbonate Description: General Toughness, Chemical Resistance, Good Surface
    Application: IT/OA (Mobile Phone) Module No.: SP2053
    High Light:

    polycarbonate granules

    ,

    polycarbonate plastic material

    PC+GF5% LUPOY SP2053 Injection Molding Grade Engineering Plastic with Good Toughness, Chemical resistance and High Impact (at Low Temperature) for Electric & Electronic (Mobile phone, Housing, TV, Components etc.), Auto Parts, IT/OA

     

     

    Quick Detail:

     

    1. Injection Molding

    2. Good Toughness

    3. Chemical resistance

    4. High Impact (at Low Temperature)

     

    Description:

     

    1. Injection Molding PC+GF5% Grade

    2. Good Toughness

    3. Chemical resistance: Chemical resistance refers to the resistance of plastics to various chemical substances. Including resistance to various acids, bases, salts solutions, organic solvents. Mainly depends on the nature of the polymer in the plastic and its composition. Most polymers have good resistance to acids, bases, and salt solutions. Some polymers containing C—O, C—N, and other bonds on the main chain are susceptible to acid and base hydrolysis and hydrolysis, resulting in degradation. The excellent chemical resistance of LUPOY GP2053 results in better mechanical Properties.

    4. High Impact (at Low Temperature)

     

    Applications:

     

    Electric & Electronic (Mobile phone, Housing, TV Components etc.), Auto Parts, IT/OA.

     

    Polycarbonate Plastic Raw Material Datasheet:

     

    Properties Test Condition Test Method Unit Typical Value
    Physical        
    Specific Gravity   ASTM D792 - 1.21
    Molding Shrinkage (Flow), 3.2mm   ASTM D955 % 0.2 ~ 0.4
    Melt Flow Rate 300℃/1.2kg ASTM D1238 g/10min 6
    Mechanical        
    Tensile Strength, 3.2mm   ASTM D638    
    @ Yield 5mm/min   kg/cm2 680
    Flexural Strength, 3.2mm 1.3mm/min ASTM D790 kg/cm2 1,100
    Flexural Modulus, 3.2mm 1.3mm/min ASTM D790 kg/cm2 29,000
    IZOD Impact Strength, 3.2mm   ASTM D256    
    (Notched) 23℃   kg·cm/cm 23
      -30℃   kg·cm/cm  
    Rockwell Hardness R-Scale ASTM D785 -  
    Thermal        
    Heat Deflection Temperature, 6.4mm   ASTM D648    
    (Unannealed) 18.6kg   135
      4.6kg    
    Vicat Softening Temperature   ASTM D1525    
      5kg, 50℃/h    
    Flammability   UL94    
    0.8mm     class HB
    1.5mm     class  
    2.5mm     class  
    3.2mm     class  
    Relative Temperature Index   UL 746B    
    Electrical     80
    Mechanical with Impact     80
    Mechanical without Impact     80

     

    Electrical      
    Comparative Tracking Index(CTI) Solution A IEC 60112 Volts
    Surface Resistivity   IEC 60093 Ohm
    Volume Resistivity 23℃ ASTM D257 Ohm·m
    Arc Resistance 23℃ ASTM D495 Ohm·cm
    Dielectric Strength, 1mm 23℃ ASTM D149 kV/mm
    Dielectric Constant (106 Hz) 23℃ ASTM D150 sec

    Good Toughness Polycarbonate Raw Material For IT/OA LUPOY SP2053 0

    Caution:

     

    1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.

    2. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.

    3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.

    4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.

    5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM

    6. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.

    7. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.

    8. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY

    9. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.

    10. THIS BAG SHOULD NOT BE USED FOR ANY OTHER PURPOSES EXCEPT FOR PACKING THE PELLETS.

    11. PLEASE REFER TO THE MATERIAL SAFETY DATA SHEET (MSDS) FOR MORE DETAILS.

    12. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.

     

     

    Good Toughness Polycarbonate Raw Material For IT/OA LUPOY SP2053 1

    Contact Details
    EVER BEST(HK) LIMITED

    Contact Person: Zhu

    Tel: +8615862380120

    Send your inquiry directly to us (0 / 3000)

    Other Products
    Request A Quote

    E-Mail | Sitemap

    Privacy Policy China Good Quality ABS Plastic Raw Material Supplier. © 2020 - 2021 polymer-plastic.com. All Rights Reserved.