LUPOY PC 8000-10 Extrusion and Injection Molding

LUPOY PC 8000-10 Extrusion and Injection Molding

  • LUPOY PC 8000-10 Extrusion and Injection Molding
  • LUPOY PC 8000-10 Extrusion and Injection Molding
  • LUPOY PC 8000-10 Extrusion and Injection Molding
LUPOY PC 8000-10 Extrusion and Injection Molding
Product Details:
Place of Origin: Korea
Brand Name: LG CHEM
Certification: MSDS, ROSH,UL
Model Number: LUPOY PC 8000-10
Payment & Shipping Terms:
Minimum Order Quantity: 16T
Price: NEGOTIABLE ACCORDING TO ORDER QUANTITY
Packaging Details: 25KG/BAG, 40BAGS PER PALLET
Delivery Time: 20 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT
Payment Terms: T/T
Supply Ability: 500T PER MONTH
Contact Now
Detailed Product Description
Color: Customer Request Shape: Particle
Usage: Small Appliances, Packaging Applications Sample: Avaiable
Type: 100% Virgin Material Name: LUPOY PC 8000-10
High Light:

pc plastic raw material

,

polycarbonate plastic material

LUPOY PC 8000-10 Extrusion and Injection Molding

Plastic Raw Material with Low Temperature Ductility, No UV Absorbers , No Mold Release Agent for Compounds, Small appliances, Packaging applications.

 

Quick Detail:

 

1. Extrusion and Injection Molding

2. Low Temperature Ductility

3. No UV Absorbers

4. No Mold Release Agent

 

Description:

 

LUPOY PC 8000-10 polycarbonate(PC) siloxane copolymer resin is designed for extrusion and injection molding products. It exhibits an excellent low temperature ductility and good physical property balance of heat resistance, transparency and impact strength.

 

Applications:

 

Compounds, Small appliances, Packaging applications

 

Datasheet:

 

  Method Value Units Value Units
Physical          
Melt Flow Rate (300 °C /1.2 kg) ASTM D 1238 0.0187 lb/10 min 8.5 g/10 min
Density ASTM D 792 75 lb/ft3 1,200 kg/m3
ISO 1183
         
Mold Shrinkage ASTM D 955 0.005~0.007 in/in 0.005~0.007 mm/mm
Water Absorption @ 24 hrs, 23°C ASTM D 570 0.12 % 0.12 %
ISO 62
         
@ equilibrium, 50%RH, 23°C ASTM D 570 0.20 % 0.20 %
ISO 62
         
Optical          
Light Transmittance (3.0mm) ASTM D 1003 >88 % >88 %
  ISO 13468-1 >88 % >88 %
Haze (3.0mm) ASTM D 1003 <1.0 % <1.0 %
  ISO/DIS 14782 <1.0 % <1.0 %
Thermal          
Deflection Temperature Under Load (DTUL) @ 3.2 mm     °F   °C
@ 66 psi (0.45 MPa), annealed ASTM D 648 269 132
@ 264 psi (1.8 MPa), annealed 266 °F 130 °C
 
@ 264 psi (1.8 MPa), unannealed   244 °F 118 °C
Deflection Temperature Under Load (DTUL)     °F   °C
@ 264 psi (1.8 MPa), unannealed ISO 75-2/A 239 115
           
Vicat Softening Point, 50°C /hr, 50N Load ASTM D 1525 280 °F 138 °C
ISO 306/B120
         
Coefficient of Linear Thermal Expansion, @ -40 to 82°C ASTM D 696 39 x 10-6 in/in/°F 70 x 10-6 mm/mm/°C
Mechanical          
Tensile Yield Strength2 ASTM D 638 8,120 psi 56 MPa
  ISO 527-2 7,980 psi 55 MPa
Ultimate Tensile Strength ASTM D 638 9,570 psi 66 MPa
  ISO 527-2 9,000 psi 62 MPa
Elongation at Yield ASTM D 638 6 % 6 %
  ISO 527-2 6 % 6 %
Elongation at Break ASTM D 638 120 % 120 %
  ISO 527-2 110 % 110 %
Tensile Modulus ASTM D 638 317,000 psi 2,180 MPa
  ISO 527-2 347,000 psi 2,390 MPa
Flexural Strength ASTM D 790 12,500 psi 86 MPa
  ISO 178 11,900 psi 82 MPa
Flexural Modulus ASTM D 790 294,000 psi 2,030 MPa
  ISO 178 281,000 psi 1,940 MPa
Notched Izod Impact3 @ 23 °C ASTM D 256 14 ft-lb/in 760 J/m
  ISO 180 28 ft-lb/in2 60 kJ/m2
Unnotched Izod Impact @ 23 °C ASTM D 256 No break   No break  
  ISO 180 No break   No break  
Notched Izod Impact3 @ -30 °C ASTM D 256 10 ft-lb/in 550 J/m
  ISO 180 21 ft-lb/in2 43 kJ/m2
Rockwell Hardness ASTM D 785 120 R Scale 50 M Scale
  ISO 2039-2
         
Electrical          
Volume Resistivity @ 23 °C, dry ASTM D 257 1.0 x 1015 W-cm 1.0 x 1015 W-cm

 

Transparent PC Plastic Granules  Caution:


1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM
6. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
7. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.
8. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY
9. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
10. THIS BAG SHOULD NOT BE USED FOR ANY OTHER PURPOSES EXCEPT FOR PACKING THE PELLETS.
11. PLEASE REFER TO THE MATERIAL SAFETY DATA SHEET (MSDS) FOR MORE DETAILS.
12. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.
 

LUPOY PC 8000-10 Extrusion and Injection Molding 0

Contact Details
EVER BEST(HK) LIMITED

Contact Person: Mr. Michael Zhu

Tel: +86 158 6238 0120

Send your inquiry directly to us (0 / 3000)

Other Products
Request A Quote

E-Mail | Sitemap

Privacy Policy China Good Quality ABS Plastic Raw Material Supplier. Copyright © 2020 - 2021 polymer-plastic.com. All Rights Reserved. Developed by ECER