PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts,

PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts,

PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts,
PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts,

Product Details:

Place of Origin: Korea
Brand Name: LG CHEM
Certification: MSDS, ROSH,UL
Model Number: GP1000DU

Payment & Shipping Terms:

Minimum Order Quantity: 16T
Price: NEGOTIABLE ACCORDING TO ORDER QUANTITY
Packaging Details: 25KG/BAG, 40BAGS PER PALLET
Delivery Time: 20 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT
Payment Terms: T/T
Supply Ability: 500T PER MONTH
Contact Now
Detailed Product Description
Place Of Origin: Guangdong,China(Mainland) Brand Nmae: LG CHEM
Material: PBT Description: General Purpose
Application: Automotive(head Lamp Bezel) Module No.: GP1000DU
High Light:

pbt plastic material

,

polyethylene terephthalate material

PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts, Electronic and Electrical products

 

PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts, 0PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts, 1

 

Quick Detail:

 

1. Injection Molding Grade

2. General Purpose

 

Description:

 

PBT Resin LUPOX GP1000DU is designed for Injection Molding. It is made for Head Lamp Bezel.

PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts, 2

 

Applications:

 

Automotive Parts, Electronic and Electrical products.

 

Datasheet:

 

Properties Test Condition Test Method Unit Typical Value
Physical        
Specific Gravity   ASTM D792 - 1.31
Mold Shrinkage, 3mm   ASTM D955 % 1.9 ~ 2.1
Mold Shrinkage, 2mm   ASTM D955 % 1.8 ~ 2.0
Melt Flow Rate 250℃/2.16kg ASTM D1238 g/10min 35
Mechanical        
Tensile Strength, 3.2mm   ASTM D638    
@ Yield 50mm/min   kg/cm2 590
Tensile Elongation, 3.2mm   ASTM D638    
@ Yield 50mm/min   % -
@ Break 50mm/min   % 100
Flexural Strength, 3.2mm 1.3mm/min ASTM D790 kg/cm2 900
Flexural Modulus, 3.2mm 1.3mm/min ASTM D790 kg/cm2 25,700
IZOD Impact Strength, 6.4mm   ASTM D256    
(Notched) 23℃   kg·cm/cm 3.5
Thermal        
Melting Temperature   ASTM D3418 223
Heat Deflection Temperature, 6.4mm   ASTM D648    
(Unannealed) 18.6kg   61
  4.6kg   174
Flammability   UL94    
0.71mm     class HB
1.5mm     class HB
3.3mm     class HB
Relative Temperature Index   UL 746B    
Electrical     140
Mechanical with Impact     130
Mechanical without Impact     140
Electrical        
Comparative Tracking Index(CTI) Solution A UL 746 PLC 0
Volume Resistivity 23℃ ASTM D257 Ohm·cm 1.0E+17
Arc Resistance 23℃ ASTM D495 PLC 5
Dielectric Strength, 1mm 23℃ ASTM D149 kV/mm 23

 

 

Processing Parameters Unit Value
Drying Temperature   120
Drying Time   hrs   5  
Maximum Moisture Content   % 0.02
Melt Temperature   245 ~ 260
  Rear 245 ~ 255
Cylinder Temperature Middle 245 ~ 260
  Front 245 ~ 260
Nozzle Temperature   250 ~ 265
Mold Temperature   30 ~ 50
Back Pressure   kg/cm2   -  
Screw Speed   rpm   -  

 

Caution:

 

1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.

2. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.

3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.

4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.

5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM

6. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.

7. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.

8. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY

9. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.

10. THIS BAG SHOULD NOT BE USED FOR ANY OTHER PURPOSES EXCEPT FOR PACKING THE PELLETS.

11. PLEASE REFER TO THE MATERIAL SAFETY DATA SHEET (MSDS) FOR MORE DETAILS.

12. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.

 

PBT Resin LUPOX GP1000DU Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts, 3

Contact Details
EVER BEST(HK) LIMITED

Contact Person: Zhu

Tel: +8615862380120

Send your inquiry directly to us (0 / 3000)

Other Products
Request A Quote

E-Mail | Sitemap

Privacy Policy China Good Quality ABS Plastic Raw Material Supplier. © 2020 - 2021 polymer-plastic.com. All Rights Reserved.