PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )

PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )

    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
    • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )
  • PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector )

    Product Details:

    Place of Origin: Korea
    Brand Name: LG CHEM
    Certification: MSDS, ROHS,UL, REACH
    Model Number: GP1000M

    Payment & Shipping Terms:

    Minimum Order Quantity: 18T
    Price: NEGOTIABLE ACCORDING TO ORDER QUANTITY
    Packaging Details: 25KG/BAG, 40BAGS PER PALLET
    Delivery Time: 30 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT
    Payment Terms: T/T
    Supply Ability: 500T PER MONTH
    Contact Now
    Detailed Product Description
    Material: PBT Resin Grade: Injection Molding
    Color: Customization Description: High Flow And High Impact
    Application: Automotive(connector) Appearance: Granules
    High Light:

    pbt plastic material

    ,

    pbt granules

    PBT Resin LUPOX GP1000M Injection Molding Grade Engineering Plastic Material with High Flow and High Impact for Automotive Parts (Connector).

     

    LUPOX GP1000M Quick Detail:

    1. Injection Molding Grade

    2. High Flow

    3. High Impact

     

    LUPOX GP1000M Description:

    PBT Resin LUPOX GP1000M is designed for Injection Molding. It exhibits excellent characteristics of High Flow and High Impact.

     

    LUPOX GP1000M Applications:

    Automotive Parts (Connector).

     

    LUPOX GP1000M Datasheet:

    Properties Test Condition Test Method Unit Typical Value
    Physical        
    Specific Gravity   ASTM D792 - 1.29
    Molding Shrinkage   ASTM D955 % 1.2 ~ 2.0
    Melt Flow Rate 250℃/2.16kg ASTM D1238 g/10min 30
    Water Absorption 23℃, 24hrs ASTM D570 % 0.08
    Mechanical        
    Tensile Strength, 3.2mm   ASTM D638    
    @ Yield 50mm/min   kg/cm2 470
    Tensile Elongation, 3.2mm   ASTM D638    
    @ Yield 50mm/min   % -
    @ Break 50mm/min   % 100
    Flexural Strength, 3.2mm 2.5mm/min ASTM D790 kg/cm2 730
    Flexural Modulus, 3.2mm 2.5mm/min ASTM D790 kg/cm2 19,000
    IZOD Impact Strength, 6.4mm   ASTM D256    
    (Notched) 23℃   kg·cm/cm 5.2
    Thermal        
    Melt Temperature   ASTM D3418 223
    Heat Deflection Temperature, 6.4mm   ASTM D648    
    (Unannealed) 18.6kg   58
      4.6kg    
    Flammability   UL94    
    0.71mm     class HB
    1.5mm     class HB
    3.3mm     class HB
    Relative Temperature Index   UL 746B    
    Electrical     140
    Mechanical with Impact     130
    Mechanical without Impact     140
    Electrical        
    Comparative Tracking Index(CTI) Solution A UL 746 PLC 0
    Volume Resistivity 23℃ ASTM D257 Ohm·cm 1.0E+17
    Arc Resistance 23℃ ASTM D495 PLC 5
    Dielectric Strength, 1mm 23℃ ASTM D149 kV/mm 23
    Processing Parameters Unit Value
    Drying Temperature   100 ~ 120
    Drying Time   hrs 4 ~ 6
    Maximum Moisture Content   % 0.02
    Melt Temperature   240 ~ 250
      Rear 230 ~ 235
    Cylinder Temperature Middle 235 ~ 240
      Front 240 ~ 245
    Nozzle Temperature   240 ~ 250
    Mold Temperature   40 ~ 80
    Back Pressure   kg/cm2   -
    Screw Speed   rpm   -

     

    LUPOX GP1000M Description:
    1. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
    2. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
    3. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM.
    4. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.

     

    PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.

     

    PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector ) 0PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector ) 1PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector ) 2PBT Resin LUPOX GP1000M PBT Raw Material With High Flow And High Impact For Automotive Parts ( Connector ) 3

    Contact Details
    EVER BEST(HK) LIMITED

    Contact Person: Zhu

    Tel: +8615862380120

    Send your inquiry directly to us (0 / 3000)

    Other Products
    Request A Quote

    E-Mail | Sitemap

    Privacy Policy China Good Quality ABS Plastic Raw Material Supplier. © 2020 - 2021 polymer-plastic.com. All Rights Reserved.