| Brand Name: | LG CHEM |
| Certification: | MSDS, ROSH,REACH |
| Model Number: | LUPOY PC 1303AH-15 |
| Minimum Order Quantity: | 18T |
|---|---|
| Price: | NEGOTIABLE ACCORDING TO ORDER QUANTITY |
| Packaging Details: | 25KG/BAG, 40BAGS PER PALLET |
| Delivery Time: | 20 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT |
| Payment Terms: | T/T |
| Supply Ability: | 500T PER MONTH |
| Type: | Virgin Polycarbonate Resin | Description: | Medium Viscosity, UV Stabilizer, Listed On AMECA And Good Mold Release Agent |
|---|---|---|---|
| Appearance: | Particles | Color: | Customer Request |
| Usage: | Automotive Headlamps, Outdoor Appliances | Grade: | Injection Molding Grade |
| High Light: | pc plastic raw material,polycarbonate plastic material |
||
LUPOY PC 1303AH-15 Injection Molding Grade Plastic Raw Material with Medium Viscosity, UV stabilizer, Listed on AMECA and Good Mold Release Agent for Appliances, Automotive headlamps, Outdoor appliances
LUPOY 1303AH-15 Quick Detail:
1. Injection Molding Grade
2. Medium Viscosity
3. UV stabilizer
4. Good Mold Release Agent
LUPOY 1303AH-15 Description:
LUPOY PC 1303AH-15 Tint Polycarbonate Resin is designed for injection molding of auto-headlamps. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.
LUPOY 1303AH-15 Applications:
Appliances, Automotive headlamps, Outdoor appliances.
LUPOY 1303AH-15 Datasheet:
| Properties | |||||
| Method | Value | Units | Value | Units | |
| Physical | |||||
| Melt Flow Rate (300 °C /1.2 kg) | ASTM D 1238 | 15 | g/10 min | 15 | g/10 min |
| Density | ASTM D 792 | 1.20 | 1,200 | kg/m3 | |
| Mold Shrinkage | ASTM D 955 | 0.005~0.007 | in/in | 0.005~0.007 | mm/mm |
| Water Absorption @ 24 hrs, 23°C | ASTM D 570 | 0.15 | % | 0.15 | % |
| @ equilibrium, 50%RH, 23°C | ASTM D 570 | 0.32 | % | 0.32 | % |
| Optical | |||||
| Refractive Index, nD | ASTM D 542 | 1.586 | 1.586 | ||
| Light Transmittance | ASTM D 1003 | 89 | % | 89 | % |
| Haze | ASTM D 1003 | 0.7~1.5 | % | 0.7~1.5 | % |
| Thermal | |||||
| Deflection Temperature Under Load (DTUL) @ 4 mm | |||||
| @ 66 psi (0.45 MPa), annealed | ASTM D 648 | 289 | °F | 143 | °C |
| @ 264 psi (1.8 MPa), annealed | ASTM D 648 | 284 | °F | 140 | °C |
| @ 264 psi (1.8 MPa), unannealed | ASTM D 648 | 260 | °F | 127 | °C |
| Vicat Softening Point, 50°C /hr, 50N Load | ASTM D 1525 | 298 | °F | 148 | °C |
| Coefficient of Linear Thermal Expansion, @ -40 to 82°C | ASTM D 696 | 38 x 10-6 | in/in/°F | 68 x 10-6 | mm/mm/°C |
| Mechanical | |||||
| Tensile Yield Strength | ASTM D 638 | 8,700 | psi | 60 | MPa |
| Ultimate Tensile Strength | ASTM D 638 | 10,300 | psi | 71 | MPa |
| Elongation at Yield | ASTM D 638 | 6 | % | 6 | % |
| Elongation at Break | ASTM D 638 | 150 | % | 150 | % |
| Tensile Modulus | ASTM D 638 | 340,000 | psi | 2,340 | MPa |
| Flexural Strength | ASTM D 790 | 14,000 | psi | 96 | MPa |
| Flexural Modulus | ASTM D 790 | 350,000 | psi | 2,410 | MPa |
| Notched Izod Impact2 @ 23 °C | ASTM D 256 | 16 | ft-lb/in | 850 | J/m |
| Unnotched Izod Impact @ 23 °C | ASTM D 256 | No break | No break | ||
| Instrumented Dart Impact3, Total Energy @ 23 °C | ASTM D 3763 | 770 | in-lb | 87 | J |
| Rockwell Hardness | ASTM D 785 | 118 | R Scale | 72 | M Scale |
| Taber Abrasion Resistance4 (D Haze) | ASTM D 1044 | 45 | % | 45 | % |
| Ignition Resistance5 | |||||
| UL-94 @ 0.5 mm | ASTM D635 | HB | HB | ||
| UL-94 @ 1.6 mm | ASTM D635 | HB | HB | ||
| UL-94 @ 2.5 mm | ASTM D635 | 26 | 26 | ||
| UL-94 @ 3.0 mm | ASTM D635 | >125 | >125 | ||
| Limiting Oxygen Index | ASTM D 2863 | 1 | % | 25 | % |
| Ball Indentation Temperature | IEC 598-1 | °C | °C | ||
| Average Extent of Burning | ASTM D 635 | 850 | in | 850 | mm |
| Electrical | 250 | 250 | |||
| GWT 2.0 mm, 5 second | IEC 695-2-1 | 420 | °C | 17 | °C |
| Compression Tracking Index @ 2.0 mm | IEC 112 | 3 | V | 3 | V |
| Dielectric Strength | ASTM D 149 | 0.001 | V/mil | 0.001 | KV/mm |
| Dielectric Constant @ 60 Hz | ASTM D 150 | 2.0 x 1017 | 2.0 x 1017 | ||
| Dissipation Factor @ 60 Hz | ASTM D 150 | 15 | 15 | ||
| Volume Resistivity @ 23 °C, dry | ASTM D 257 | 1.20 | W-cm | 1,200 | W-cm |
LUPOY 1303AH-15 Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM
6. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
7. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.
8. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY
9. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
10. THIS BAG SHOULD NOT BE USED FOR ANY OTHER PURPOSES EXCEPT FOR PACKING THE PELLETS.
11. PLEASE REFER TO THE MATERIAL SAFETY DATA SHEET (MSDS) FOR MORE DETAILS.
12. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.
,
Contact Person: Mr. Michael Zhu
Tel: +86 158 6238 0120