| Place of Origin: | Korea |
| Brand Name: | LG CHEM |
| Certification: | MSDS,ROHS, REACH |
| Model Number: | ASA LI942 |
| Minimum Order Quantity: | 18T |
|---|---|
| Price: | NEGOTIABLE ACCORDING TO ORDER QUANTITY |
| Packaging Details: | 25KG/BAG, 40BAGS PER PALLET |
| Delivery Time: | 30 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT |
| Payment Terms: | T/T |
| Supply Ability: | 500T PER MONTH |
| Material Type: | ASA Resin | Material Grade: | Injection Molding Grade |
|---|---|---|---|
| Appearance: | Particles | Material Color: | Customization Is Available |
| Descriptions: | Injection Molding,Good Weatherability,High Heat Resistance | Application: | Roof Rack Cover, Garnish, Grill, Radiator Grill, Side Mirror |
| High Light: | asa plastic material,asa granules |
||
ASA LI942 Injection Molding Grade Plastic Raw Material with Good Weatherability and High Heat Resistance for Outdoor Products, Air Conditioning Grilles, Automotive Part (Roof Rack Cover, Garnish, Grill, Radiator Grill, Side Mirror).
ASA LI942 Quick Detail:
1. Injection Molding
2. Good Weatherability
3. High Heat Resistance
ASA LI942 Description:
1. Injection Molding ASA grade
2. Good Weatherability : ASA LI942 material is specially used for outdoor products that need long-term resistance to ultraviolet rays and various hot and humid weather.
3. High Heat Resistance: ASA LI942 material's HDT is 99℃.
ASA LI942 Applications:
Outdoor Products, Air Conditioning Grilles, Automotive Part (Roof Rack Cover, Garnish, Grill, Radiator Grill, Side Mirror).
ASA LI942 Datasheet:
| Properties | Test Condition | Test Method | Unit | Typical Value |
| Physical | ||||
| Density | ISO 1183 | g/cm3 | 1.09 | |
| Molding Shrinkage (Flow), 3.2mm | ISO 294-4 | % | 0.4~0.7 | |
| Melt Flow Rate | 220℃/10kg | ISO 1133 | g/10min | 3.0 |
| Mechanical | ||||
| Tensile Strength | ISO 527 | |||
| @ Yield | 50mm/min | MPa | 48 | |
| Tensile Modulus | 1mm/min | ISO 527 | MPa | 2,250 |
| Flexural Strength | 2mm/min | ISO 178 | MPa | 75 |
| Flexural Modulus | 2mm/min | ISO 178 | MPa | 2,400 |
| IZOD Impact Strength, 80*10*4mm | ISO 180/1A | |||
| (Notched) | 23℃ | kJ/m2 | 8.0 | |
| -30℃ | kJ/m2 | - | ||
| Charpy Impact Strength, 80*10*4mm | ISO179/1eA | |||
| (Notched) | 23℃ | kJ/m2 | 8.0 | |
| -30℃ | kJ/m2 | - | ||
| Rockwell Hardness | ISO 2039 | - | 110 | |
| Thermal | ||||
| Heat Deflection Temp. 120*10*4mm | ||||
| 1.8MPa | ISO 75/Be | ℃ | 91 | |
| 0.45MPa | ISO 75/Ae | ℃ | ||
| Vicat Softening Temperature | ||||
| 50N, 50℃/h | ISO 306 | 105 | ||
| Flammability | UL94 | |||
| Relative Temperature Index | UL 746B | |||
| Electrical | ℃ | - | ||
| Mechanical with Impact | ℃ | - | ||
| Mechanical without Impact | ℃ | - | ||
| Electrical | ||||
| Comparative Tracking Index(CTI) | Solution A | IEC 60112 | Volts | - |
| Surface Resistivity | IEC 60093 | Ohm | - | |
| Volume Resistivity | 23℃ | IEC 60093 | Ohm·m | - |
| Electric Strength, 1mm | 23℃ | IEC 60243-1 | kV/mm | - |
| Processing Parameters | Unit | Value | ||
| Drying Temperature | ℃ | 70 | ~ 80 | |
| Drying Time | hrs | 3 | ~ 4 | |
| Minimum Moisture Content | % | 0.07 | ||
| Melt Temperature | ℃ | 200 | ~ 220 | |
| Rear | ℃ | 210 | ~ 230 | |
| Cylinder Temperature | Middle | ℃ | 220 | ~ 240 |
| Front | ℃ | 230 | ~ 250 | |
| Nozzle Temperature | ℃ | 230 | ~ 250 | |
| Mold Temperature | ℃ | 40 | ~ 60 | |
| Back Pressure | kg/cm2 | 10~30 | ||
| Screw Speed | RPM | Low Speed | ||
ASA LI942 Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
3. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
4. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
5. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY.
Contact Person: Mr. Michael Zhu
Tel: +86 158 6238 0120