| Place of Origin: | Korea |
| Brand Name: | LG CHEM |
| Certification: | MSDS, ROHS, REACH |
| Model Number: | ASA LI951 |
| Minimum Order Quantity: | 18T |
|---|---|
| Price: | NEGOTIABLE ACCORDING TO ORDER QUANTITY |
| Packaging Details: | 25KG/BAG, 40BAGS PER PALLET |
| Delivery Time: | 30 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT |
| Payment Terms: | T/T |
| Supply Ability: | 500T PER MONTH |
| Product Type: | ASA Resin | Material Grade: | Injection Molding Grade |
|---|---|---|---|
| Sharp: | Granules | Product Color: | Natural Color Or Customized Color |
| Descriptions: | Injection Molding,Good Weatherability,High Heat Resistance | Application: | Outdoor Products,Garnish, Grill |
| High Light: | asa granules,asa resin |
||
ASA LI951 Injection Molding Grade Plastic Raw Material with Good Weatherability and High Heat Resistance for Outdoor Products, Air Conditioning Grilles, Automotive Part (Roof Rack Cover, Garnish, Grill, Radiator Grill, Side Mirror).
ASA LI951 Quick Detail:
1. Injection Molding
2. Good Weatherability
3. High Heat Resistance
ASA LI951 Description:
1. Injection Molding ASA grade
2. Good Weatherability : ASA LI951 material is specially used for outdoor products that need long-term resistance to ultraviolet rays and various hot and humid weather.
3. High Heat Resistance: ASA LI951 material's HDT is 95℃.
ASA LI951 Applications:
Outdoor Products, Air Conditioning Grilles, Automotive Part (Roof Rack Cover, Garnish, Grill, Radiator Grill, Side Mirror).
ASA LI951Datasheet:
| Properties | Test Condition | Test Method | Unit | Typical Value |
| Physical | ||||
| Specific Gravity | ASTM D792 | - | 1.08 | |
| Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.4~0.7 | |
| Melt Flow Rate | 220℃/10kg | ASTM D1238 | g/10min | 6 |
| Mechanical | ||||
| Tensile Strength, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | kg/cm2 | 510 | |
| Tensile Elongation, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | % | ||
| @ Break | 50mm/min | % | 25 | |
| Tensile Modulus, 3.2mm | 1mm/min | ASTM D638 | kg/cm2 | |
| Flexural Strength, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | 790 |
| Flexural Modulus, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | 24,000 |
| IZOD Impact Strength, 6.4mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | 11 | |
| -30℃ | kg·cm/cm | |||
| IZOD Impact Strength, 3.2mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | ||
| -30℃ | kg·cm/cm | |||
| Rockwell Hardness | R-Scale | ASTM D785 | - | 104 |
| Thermal | ||||
| Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
| (Unannealed) | 18.6kg | ℃ | 95 | |
| 4.6kg | ℃ | |||
| Vicat Softening Temperature | ASTM D1525 | |||
| 5kg, 50℃/h | ℃ | 104 | ||
| Flammability | UL94 | |||
| Relative Temperature Index | UL 746B | |||
| Electrical | ℃ | |||
| Mechanical with Impact | ℃ | |||
| Mechanical without Impact | ℃ | |||
| Optical | ||||
| Gloss | 45˚ | ASTM D2457 | - |
| Processing Parameters | Unit | Value | ||
| Drying Temperature | ℃ | 70 | ~ 80 | |
| Drying Time | hrs | 3 | ~ 4 | |
| Minimum Moisture Content | % | 0.07 | ||
| Melt Temperature | ℃ | 190 | ~ 210 | |
| Rear | ℃ | 200 | ~ 220 | |
| Cylinder Temperature | Middle | ℃ | 210 | ~ 230 |
| Front | ℃ | 220 | ~ 240 | |
| Nozzle Temperature | ℃ | 220 | ~ 240 | |
| Mold Temperature | ℃ | 40 | ~ 60 | |
| Back Pressure | kg/cm2 | 10~30 | ||
| Screw Speed | RPM | Low Speed | ||
ASA LI951 Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
3. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM
4. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY
5. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
Contact Person: Mr. Michael Zhu
Tel: +86 158 6238 0120