One-stop sourcing for global plastic customers.
Become solution partner for our customers.
 
|
| Place of Origin: | Korea |
| Brand Name: | LG CHEM |
| Certification: | MSDS,ROHS, REACH |
| Model Number: | ASA LI968W |
| Minimum Order Quantity: | 18T |
|---|---|
| Price: | NEGOTIABLE ACCORDING TO ORDER QUANTITY |
| Packaging Details: | 25KG/BAG, 40BAGS PER PALLET |
| Delivery Time: | 30 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT |
| Payment Terms: | T/T |
| Supply Ability: | 500T PER MONTH |
| Features: | Scratch-resistance | Material: | ASA Resin |
|---|---|---|---|
| Product Grade: | Co-Extrusion Grade | Appearance: | Particles |
| Material Color: | Customization For Color Is Available | Application: | Window Profiles, Exterior Materials |
| High Light: | asa plastic material,asa granules |
||
ASA LI968W Co-Extrusion Grade Plastic Raw Material with Good Weatherability and Scratch-resistance for Canopy, Siding, Fence, Window profiles, Exterior Materials, Roof Tiles, Rain Gutters.
ASA LI968W Quick Detail:
1. Co-Extrusion
2. Good Weatherability
3. Scratch-resistance
ASA LI968W Description:
1. Co-Extrusion ASA grade
2. Good Weatherability : ASA LI968W material is specially used for outdoor products that need long-term resistance to ultraviolet rays and various hot and humid weather.
ASA LI968W Applications:
Canopy, Siding, Fence, Window profiles, Exterior Materials, Roof Tiles, Rain Gutters.
ASA LI968W Datasheet:
| Properties | Method | Unit | LI968W |
| Physical | |||
| Specific Gravity , 23℃ | ASTM D792 | 1.09 | |
| Mold Shrinkage , 23℃, 3.2mm , 23℃ | ASTM D955 | % | 0.4 ~ 0.7 |
| Melt Flow Rate , 220℃, 10kg | ASTM D1238 | g/10min | 11 |
| Mechanical | |||
| Tensile Strength at Yield , 23℃, 50mm/min, 3.2mm | ASTM D638 | Mpa | 49 |
| Tensile Elongation at Yield , 23℃, 50mm/min, 3.2mm | ASTM D638 | %, (Min) | 6 |
| Tensile Elongation at Break , 23℃, 50mm/min, 3.2mm | ASTM D638 | %, (Min) | 25 |
| Tensile Modulus , 23℃, 50mm/min, 3.2mm | ASTM D638 | MPa | 2140 |
| Flexural Strength , 23℃, 15mm/min, 3.2mm | ASTM D790 | Mpa | 77 |
| Flexural Modulus , 23℃, 15mm/min, 3.2mm | ASTM D790 | MPa | 2350 |
| Izod Impact Strength , Notched, 3.2mm, 23℃ | ASTM D256 | J/m | 175 |
| Izod Impact Strength , Notched, 3.2mm, -30℃ | ASTM D256 | J/m | 40 |
| Izod Impact Strength , Notched, 6.4mm, 23℃ | ASTM D256 | J/m | 135 |
| Izod Impact Strength , Notched, 6.4mm, -30℃ | ASTM D256 | J/m | 40 |
| Rockwell Hardness , R-Scale | ASTM D785 | 102 | |
| Thermal | |||
| HDT , Edgewise, 1.82MPa, 6.4mm, Unannealed | ASTM D648 | ℃ | 86 |
| VICAT , 50N, 50℃/h | ASTM D1525 | ℃ | 95 |
| Processing Guide (Extrusion Molding) | |||
| Processing Parameters | Unit | Value | |
| Drying Temperature | ℃ | 80 | ~ 90 |
| Drying Time | hrs | 2 | ~ 3 |
| Minimum Moisture Content | % | 0.01 | ~ 0.01 |
| Melt Temperature | ℃ | 200 | ~ 230 |
| Barrel Temperature, Zone 1 | ℃ | 190 | ~ 200 |
| Barrel Temperature, Zone 2 | ℃ | 200 | ~ 220 |
| Barrel Temperature, Zone 3 | ℃ | 210 | ~ 230 |
| Barrel Temperature, Zone 4 | ℃ | 210 | ~ 230 |
| Adapter Temperature | ℃ | 210 | ~ 230 |
| Die Temperature | ℃ | 210 | ~ 250 |
| Roll Stack Temperature, Top | ℃ | 70 | ~ 90 |
| Roll Stack Temperature, Middle | ℃ | 70 | ~ 90 |
| Roll Stack Temperature, Bottom | ℃ | 70 ~ 100 | |
ASA LI968W Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
3. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
4. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM.
5. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.