| Place of Origin: | Korea |
| Brand Name: | LG CHEM |
| Certification: | MSDS, ROHS, REACH |
| Model Number: | TPE KEYFLEX BT 1182D |
| Minimum Order Quantity: | 18T |
|---|---|
| Price: | NEGOTIABLE ACCORDING TO ORDER QUANTITY |
| Packaging Details: | 25KG/BAG, 40BAGS PER PALLET |
| Delivery Time: | 30 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT |
| Payment Terms: | T/T |
| Supply Ability: | 500T PER MONTH |
| Product Name: | TPE Raw Material | Brand Nmae: | LG CHEM |
|---|---|---|---|
| Material: | TPE | Description: | Injection Molding Grade |
| Application: | Automotive Body Plug, Fastener | Module No.: | TPE KEYFLEX BT 1182D |
| High Light: | tpe plastic material,tpe granules |
||
Ester Type TPE KEYFLEX TPE Raw Material BT 1182D with High Modulus for Cable & Wire Jackets, Hose & Tubing, Sheet.
BT 1182D Quick Detail:
1. Injection Molding Grade
2. General Purpose
3. High Modulus
4. Ester Type TPE
BT 1182D Description:
Ester Type TPE KEYFLEX BT 1182D is designed for injection molding products. It exhibits an excellent characteristic of High Modulus.
BT 1182D Applications:
Cable & Wire Jackets, Hose & Tubing, Sheet.
BT 1182D Datasheet:
| Properties | Test Condition | Test Method | Unit | Typical Value |
| Physical | ||||
| Specific Gravity | ASTM D792 | - | 1.28 | |
| Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 1.4 ~ 1.8 | |
| Melt Flow Rate | 240℃/2.16kg | ASTM D1238 | g/10min | 16 |
| Water Absorption | 23℃, 24hrs | ASTM D570 | % | 0.3 |
| Mechanical | ||||
| Tensile Strength, 2mm | ASTM D638 | |||
| @ Yield | 50mm/min | kg/cm2 | 350 | |
| @ Break | 50mm/min | kg/cm2 | 500 | |
| Tensile Elongation, 2mm | ASTM D638 | |||
| @ Yield | 50mm/min | % | ||
| @ Break | 50mm/min | % | 350 | |
| Flexural Strength, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | |
| Flexural Modulus, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | 11,000 |
| Tear Strength @ Break | 50mm/min | ASTM D624 | kg/cm | 170 |
| IZOD Impact Strength, 6.4mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | 4 | |
| -40℃ | kg·cm/cm | 3 | ||
| Shore Hardness | Shore D | ASTM D2240 | - | 74 |
| Shore Hardness | Shore A | ASTM D2240 | - | |
| Thermal | ||||
| Melt Temperature @ Peak | ASTM D3418 | ℃ | 220 | |
| Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
| (Unannealed) | 4.6kg | ℃ | 145 | |
| Electrical | ||||
| Comparative Tracking Index(CTI) | Solution A | IEC 60112 | Volts | 600 |
| Surface Resistivity | IEC 60093 | Ohm | ||
| Volume Resistivity | 23℃ | ASTM D257 | Ohm·m | >E11 |
| Dielectric Strength, 1mm | 23℃ | ASTM D149 | kV/mm | 26 |
| Dielectric Constant (106 Hz) | 23℃ | ASTM D150 | sec |
BT 1182D Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2.KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4.LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY
5. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
FOR MORE INFORMATION, PLEASE CONTACT US.