Material: | PA66+GF30% Resin | Description: | General Purpose |
---|---|---|---|
Grade: | Injection Molding Grade | Form: | Particles |
Application: | Automotive Parts,Electric & Electronic Parts. | Color: | Customization For Color Is Available |
High Light: | polyamide granules,pa raw material |
PA66+GF30% Resin LUMID GP2300B(W) Resin Injection Molding Grade Engineering Plastic Material with General Purpose for Automotive Parts,Electric & Electronic Parts.
LUMID GP2300B(W) Quick Detail:
1. Injection Molding Grade
2. General Purpose
3. PA66+GF30%
LUMID GP2300B(W) Description:
PA66+GF30% LUMID GP2300B(W) Resin is designed for Injection Molding.
LUMID GP2300B(W) Applications:
Automotive Parts,Electric & Electronic Parts.
LUMID GP2300B(W) Datasheet:
Properties | Test Condition | Test Method | Unit | Typical Value |
Physical | ||||
Specific Gravity | ASTM D792 | - | 1.37 | |
Molding Shrinkage, 3.2mm | ASTM D955 | % | 0.4~0.9 | |
Melt Flow Rate | ASTM D1238 | g/10min | ||
Water Absorption | 23℃, 24hrs | ASTM D570 | % | 1.1 |
Mechanical | ||||
Tensile Strength, 3.2mm | ASTM D638 | |||
@ Break | 5mm/min | kg/cm2 | 1,800 | |
Tensile Elongation, 3.2mm | ASTM D638 | |||
@ Break | 5mm/min | % | 2.9 | |
Flexural Strength, 6.4mm | 3mm/min | ASTM D790 | kg/cm2 | 2,500 |
Flexural Modulus, 6.4mm | 3mm/min | ASTM D790 | kg/cm2 | 87,500 |
IZOD Impact Strength, 6.4mm | ASTM D256 | |||
(Notched) | 23℃ | kg·cm/cm | 10 | |
-30℃ | kg·cm/cm | |||
Thermal | ||||
Melting Temperature | ASTM D3418 | ℃ | 260 | |
Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
(Unannealed) | 18.6kg | ℃ | 255 | |
4.6kg | ℃ | |||
Coefficient of Linear Thermal Expansion | ASTM D696 | |||
Flow | 10-5 m/m℃ | 3 | ||
Cross-flow | 10-5 m/m℃ | |||
Ball Pressure Temperature | IEC 60695-10-2 | ℃ | ||
Burning Rate, 3.2mm | FMVSS 302 | mm | ||
Flammability | UL94 | |||
0.75mm | class | HB | ||
1.5mm | class | HB | ||
3.0mm | class | HB | ||
Relative Temperature Index | UL 746B | |||
Electrical | 120 | ℃ | ||
Mechanical with Impact | 110 | ℃ | ||
Mechanical without Impact | 120 | ℃ |
LUMID GP2300B(W) Caution:
1. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
2. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
3. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
4. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM.
5. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
FOR MORE INFOMATION, PLEASE CONTACT US.
Contact Person: Mr. Michael Zhu
Tel: +86 158 6238 0120