| Place of Origin: | Korea |
| Brand Name: | LG CHEM |
| Certification: | MSDS, ROSH,UL |
| Model Number: | GP1000SB |
| Minimum Order Quantity: | 16T |
|---|---|
| Price: | NEGOTIABLE ACCORDING TO ORDER QUANTITY |
| Packaging Details: | 25KG/BAG, 40BAGS PER PALLET |
| Delivery Time: | 20 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT |
| Payment Terms: | T/T |
| Supply Ability: | 500T PER MONTH |
| Place Of Origin: | Guangdong,China(Mainland) | Brand Nmae: | LG CHEM |
|---|---|---|---|
| Material: | PBT | Description: | Anti-hydrolysis |
| Application: | Automotive(connector) | Module No.: | GP1000SB |
| High Light: | pbt plastic material,pbt granules |
||
PBT Resin LUPOX GP1000SB Injection Molding Grade Engineering Plastic Material with Anti-Hydrolysis for Automotive Parts (Connector)
Quick Detail:
1. Injection Molding Grade
2. Anti-Hydrolysis
Description:
PBT Resin LUPOX GP1000SB is designed for Injection Molding. It is made for Connector.
Applications:
Automotive Parts (Connector)
Datasheet:
| Properties | Test Condition | Test Method | Unit | Typical Value |
| Physical | ||||
| Specific Gravity | ASTM D792 | - | 1.30 | |
| Molding Shrinkage | ASTM D955 | % | 1.2 ~ 2.0 | |
| Melt Flow Rate | 235℃/2.16kg | ASTM D1238 | g/10min | 16 |
| Water Absorption | 23℃, 24hrs | ASTM D570 | % | 0.08 |
| Mechanical | ||||
| Tensile Strength, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | kg/cm2 | 510 | |
| Tensile Elongation, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | % | - | |
| @ Break | 50mm/min | % | 100 | |
| Flexural Strength, 3.2mm | 2.5mm/min | ASTM D790 | kg/cm2 | 800 |
| Flexural Modulus, 3.2mm | 2.5mm/min | ASTM D790 | kg/cm2 | 22,000 |
| IZOD Impact Strength, 6.4mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | 5.6 | |
| Thermal | ||||
| Melt Temperature | ASTM D3418 | ℃ | 223 | |
| Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
| (Unannealed) | 18.6kg | ℃ | 57 | |
| 4.6kg | ℃ | |||
| Flammability | UL94 | |||
| 0.71mm | class | HB | ||
| 1.5mm | class | HB | ||
| 3.3mm | class | HB | ||
| Relative Temperature Index | UL 746B | |||
| Electrical | ℃ | 140 | ||
| Mechanical with Impact | ℃ | 130 | ||
| Mechanical without Impact | ℃ | 140 | ||
| Electrical | ||||
| Comparative Tracking Index(CTI) | Solution A | UL 746 | PLC | 0 |
| Volume Resistivity | 23℃ | ASTM D257 | Ohm·cm | 1.0E+17 |
| Arc Resistance | 23℃ | ASTM D495 | PLC | 5 |
| Dielectric Strength, 1mm | 23℃ | ASTM D149 | kV/mm | 23 |
Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM
6. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
7. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.
8. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY
9. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
10. THIS BAG SHOULD NOT BE USED FOR ANY OTHER PURPOSES EXCEPT FOR PACKING THE PELLETS.
11. PLEASE REFER TO THE MATERIAL SAFETY DATA SHEET (MSDS) FOR MORE DETAILS.
12. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.
Contact Person: Mr. Michael Zhu
Tel: +86 158 6238 0120