One-stop sourcing for global plastic customers.
Become solution partner for our customers.
 
|
| Place of Origin: | Korea |
| Brand Name: | LG CHEM |
| Certification: | MSDS,ROHS, REACH |
| Model Number: | SAN 80HFICELLHK |
| Minimum Order Quantity: | 18T |
|---|---|
| Price: | NEGOTIABLE ACCORDING TO ORDER QUANTITY |
| Packaging Details: | 25KG/BAG, 40BAGS PER PALLET |
| Delivery Time: | 30 WOKING DAYS UPON RECEIPT OF ORDER CONFIRMATION AND PAYMENT |
| Payment Terms: | T/T |
| Supply Ability: | 500T PER MONTH |
| Material: | SAN Resin | Form: | Particles |
|---|---|---|---|
| Product Grade: | Injection Molding Grade | Descriptions: | High Transparency, Heat And Chemical Resistance |
| Usage: | Customized Color | Product Color: | Refrigerator Sleeves, Fan Impeller, Food Container, Cosmetic Housing And Daily Necessities |
| High Light: | styrene acrylonitrile copolymer,san styrene acrylonitrile |
||
SAN 80HFICELLHK Injection Molding Grade Plastic Raw Material with High Transparency, Heat Resistance and Chemical Resistance for Refrigerator Sleeves, Fan Impeller, Food Container, Cosmetic Housing and Daily Necessities.
SAN 80HFICELLHK Quick Detail:
1. Injection Molding
2. High Transparency
3. Heat Resistance
4. Chemical Resistance
5. Widely Used Grade
SAN 80HFICELLHK Description:
1. Injection molding SAN grade
2. High Transparency: the luminous transmittance is about 87% to 90%
3. Heat Resistance: 80HFICELLHK has high heat resistance, and its HDT is about 90℃.
4. Chemical Resistance: Very strong chemical resistance.
5. Widely Used Grade: This is widely used SAN grade
SAN 80HFICELLHK Applications:
Refrigerator Sleeves, Fan Impeller, Food Container, Cosmetic Housing and Daily Necessities.
SAN 80HFICELLHK Datasheet:
| Properties | Test Condition | Test Method | Unit | Typical Value |
| Physical | ||||
| Specific Gravity | ASTM D792 | - | 1.07 | |
| Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.2~0.6 | |
| Melt Flow Rate | 200℃/5kg | ASTM D1238(G) | g/10min | 2.5 |
| 220℃/10kg | - | g/10min | 25 | |
| 230℃/3.8kg | ASTM D1238(I) | g/10min | 9 | |
| Mechanical | ||||
| Tensile Strength, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | kg/cm2 | 740 | |
| Tensile Elongation, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | % | ||
| @ Break | 50mm/min | % | 6 | |
| Tensile Modulus, 3.2mm | 1mm/min | ASTM D638 | kg/cm2 | |
| Flexural Strength, 3.2mm | 15mm/min | ASTM D790 | kg/cm2 | 1,230 |
| Flexural Modulus, 3.2mm | 15mm/min | ASTM D790 | kg/cm2 | 37,500 |
| IZOD Impact Strength, 6.4mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | 1 | |
| -30℃ | kg·cm/cm | |||
| IZOD Impact Strength, 3.2mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | ||
| -30℃ | kg·cm/cm | |||
| Rockwell Hardness | R-Scale | ASTM D785 | - | 123 |
| Thermal | ||||
| Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
| (Unannealed) | 18.6kg | ℃ | 90 | |
| 4.6kg | ℃ | |||
| Vicat Softening Temperature | ASTM D1525 | |||
| 5kg, 50℃/h | ℃ | 100 | ||
| Flammability | UL94 | |||
| 1.5mm | class | HB | ||
| 3.0mm | class | HB | ||
| Relative Temperature Index | UL 746B | |||
| Electrical | ℃ | - | ||
| Mechanical with Impact | ℃ | - | ||
| Mechanical without Impact | ℃ | - |
| Processing Parameters | Unit | Value | ||
| Drying Temperature | ℃ | 80 | ||
| Drying Time | hrs | 2 | ~ 4 | |
| Minimum Moisture Content | % | 0.01 | ||
| Melt Temperature | ℃ | 190 | ~ 220 | |
| Rear | ℃ | 170 | ~ 190 | |
| Cylinder Temperature | Middle | ℃ | 180 | ~ 200 |
| Front | ℃ | 190 | ~ 210 | |
| Nozzle Temperature | ℃ | 190 | ~ 220 | |
| Mold Temperature | ℃ | 40 | ~ 70 | |
| Back Pressure | kg/cm2 | 300 | ~ 600 | |
| Screw Speed | rpm | 30 | ~ 60 | |
SAN 80HFICELLHK Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM.
Contact Person: Mr. Michael Zhu
Tel: +86 158 6238 0120